Applications
Welding of 0.5% Cr-1% Mo steels used for electric power and high pressure vessel.
Notes on usage
(1) Dry the electrodes at 350-400°C for about one hour before use and store the electrodes at 100-150°C after drying them with attention to keep away from moisture.
(2) Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blowholes at the arc starting.
(3) Keep the arc as short as possible
(4) Preheat at 100-150°C. The temperature to be applied varies in accordance with plate thickness and kind of steel to be welded.
(5) Pay attention not to exceed proper heat-input because excessive heat-input causes deterioration of impact values and yield strength of weld metal.
Typical Chemical Composition of Weld Metal (%):
C |
Si |
Mn |
Cr |
Mo |
0.09 |
0.56 |
0.42 |
0.54 |
1.08 |
Typical Mechanical Properties of Weld Metal:
Yield Point
N/mm2 (Kgf/mm2) |
Tensile Strength
N/mm2 (Ksi) |
Elongation
(%) |
PWHT |
570 (83) |
650 ((94) |
26 |
690 degrees C x ` hr |
Size and Recommended Current Range (AC/DC+):
Diameter (mm) |
2.5 |
3.2 |
4.0 |
5.0 |
Length (mm) |
350 |
350 |
400 |
400 |
Ampere |
Flat |
55-85 |
90-130 |
130-180 |
180-240 |
V & OH |
50-80 |
80-115 |
110-170 |
150-200 |
Welding Positions:
ALL POSITIONS
Packing:
20 Kg corrugated box, with 4 units of 5 Kg shrinked plastic wrapped paper boxes inside.
Special requests on packing are accepted. |